Equipment pipeline anti-corrosion silicone high-temperature resistant paint

Product Introduction:

Silicone high-temperature resistant paint is used for rust prevention and decoration of metal under high-temperature conditions. Silicone high-temperature resistant coating is composed of specialized silicone resin, special high-temperature resistant pigments, special additives, solvents, and other agents.

Main Features:

◆ Corrosion resistance: Silicone high-temperature resistant paint resists chemical atmosphere, acid and alkali, damp heat, and protects the substrate from corrosion.

◆ Temperature resistance: Long-term resistance to high temperatures of 100-600°C, without cracking or powdering of the paint film.

◆ Thermal cycling resistance: Withstands over 10 cycles of cold and heat; the coating does not peel under drastic temperature changes.

◆ Decorative properties: The paint film comes in various colors with good decorative effects and does not discolor under high temperatures.

◆ Mechanical properties: High hardness, good toughness, wear resistance, and scratch resistance.

◆ Application performance: Fast drying and good construction properties.

Applications:

◆ Suitable as a specialized anti-corrosion primer for steel structures, storage tanks, bridges, docks, chemical plants, fertilizer plants, power plants, oil refineries, paper mills, and sewage treatment plants. Also used as a specialized coating for chimneys, flues, drying ovens, exhaust pipes, hot blast stoves, high-temperature gas pipes, and other equipment requiring high-temperature corrosion resistance.

Basic Parameters

Color: Black, iron red, gray, silver. Gloss: Matte

Solid content: 60%

Dry film thickness: 30 μm

Theoretical consumption: 200g/m²

Flash point: 25°C

Drying time (25°C): Surface dry ≤1.5h, hard dry ≤24h, full cure 7d

Recoat interval:

Substrate temperature: 5°C      25°C      40°C

Minimum: 48h     24h       16h

Maximum: Unlimited

Surface Preparation

All surfaces must be clean, dry, and free from contamination. Evaluation and treatment should follow ISO 8504.

Bare steel cleanliness: Blast cleaning to Sa2.5 grade (ISO 8501-1:1998).

Depending on the situation, power tool cleaning may also be used, with a minimum of St2 grade and no scale (ISO 8501-1:1988).

Steel with shop primer: Clean, dry, and intact approved shop primer.

Painted surfaces: Clean, dry, and intact compatible primer.

Recommended Coating Layers: ◆ Airless spray: 1 coat; brush or roller: 1-2 coats.

Compatible Primer:  ◆ Inorganic zinc-rich paint, inorganic zinc silicate paint, silicone high-temperature resistant primer.

Surface Treatment:   Steel surface blast cleaned to Sa2.5 grade, surface roughness 30μm-75μm.

◆ Power tool cleaning to St3 grade.

Application Methods

Substrate temperature must be above 3°C, and relative humidity must be below 85%. When the substrate temperature is between 30°C and 60°C, spraying must be used.

Coating application:

Airless spray: Nozzle size 0.4mm-0.5mm, output pressure 20MPa-25MPa (200kg/cm²-250kg/cm²), dilution ratio 0-5%.

Conventional spray: Nozzle size 1.5mm-2.0mm, output pressure 0.3MPa-0.4MPa (3kg/cm²-4kg/cm²), dilution ratio 10%-15%.

Roller application: Dilution ratio 5%-10%.

Thinner: Special silicone thinner

Specification: 20kg/drum

Remarks:

Statement 1: Although the above data are based on tests and accumulated application experience and can serve as a reference for construction, most parameters in practical applications depend on factors such as film thickness, application environment (ventilation, temperature, humidity, etc.), underlying coating/overall compatibility, etc.

2. This product is only suitable for professional use. For applications not specified or under conditions unknown to us, we only guarantee the quality of the coating itself.

3. This manual has been updated and improved based on our recent accumulation and summary of construction practices. This version replaces all previous versions.

4. We will continue to summarize, update, and improve through future construction practices. We sincerely welcome valuable feedback from both new and existing users during application. Please contact us promptly for the latest manual via phone or mail. Thank you for your cooperation!